Registro completo de metadatos
Campo DC Valor Lengua/Idioma
dc.contributor.advisorOrna Chávez, Javier Enrique-
dc.contributor.authorGusqui Martinez, Estefania Paulina-
dc.contributor.authorRivera Enriquez, Marco Ivan-
dc.date.accessioned2019-04-02T19:56:36Z-
dc.date.available2019-04-02T19:56:36Z-
dc.date.issued2018-11-06-
dc.identifier.citationGusqui Martinez, Estefania Paulina; Rivera Enriquez, Marco Ivan. (2018). Diseño y construcción de un prototipo para la obtención de polvo metalico a partir de la viruta generada de los procesos de mecanizado del CIRT unidad de negocios Hidroagoyan. Escuela Superior Politécnica de Chimborazo. Riobamba.es_ES
dc.identifier.urihttp://dspace.espoch.edu.ec/handle/123456789/10179-
dc.descriptionEn la propuesta tecnológica que se presenta, se realizó el diseño y construcción del prototipo para la obtención de polvo metálico a partir de la viruta generada del proceso de mecanizado, para lo cual fue necesario el análisis bibliográfico y estudio de las técnicas de obtención de polvo, se selecciona la alternativa más conveniente para lograr dicho objetivo mediante el uso de la matriz QFD y método de los criterios ponderados, el molino planetario de bolas, luego se procedió al diseño mecánico y selección de cada elemento que conforma el prototipo, usando herramientas de simulación: SOLIDWORKS, ANSYS, ADAMS Y SAP2000. Posteriormente se desarrolló los planos de los elementos, mediante la elaboración de flujogramas de procesos se realizó dicha construcción y montaje del prototipo. Las pruebas de funcionamiento se realizaron con bronce, acero de transmisión y Acero ASTM A743, a una capacidad máxima de alimentación de 220 gr y una velocidad de 400 RPM durante dos, cuatro y cinco horas, con 25 bolas de acero templado de 20 mm durante la primera y segunda hora de molienda, usando en el tiempo restante 100 de ϕ10 mm, posteriormente se tamizo el polvo teniendo 153 gr de bronce entre 0,6 a 0,06 mm y 69 gr ≤ a 0,06 mm de donde el 57,14% está en un rango de 2,49 a 9,74 µm, en el de transmisión se tiene 143 gr entre 0,4 a 0,06 mm y 76 gr debajo de estos límites con un 58,57% entre 1,02 a 4,72 µm, en el inoxidable 129 gr tienen de 1 a 0,06 mm de donde 86 gr son menores con un 78,57% entre 2,13 a 8,45 µm, se concluye entonces que si es posible obtener polvo metálico de acero inoxidable especialmente. Se sugiere seguir las recomendaciones presentadas con el fin de ampliar esta investigación.es_ES
dc.description.abstractIn the technological proposal presented, the design and construction of the prototype were carried out to obtain metallic powder from the chip generated from the machining process, For which it was necessary the bibliographic analysis and study of the techniques of obtaining a powder, the most convenient alternative is selected to achieve this objective through the use of the QFD matrix and the weighted criteria method, the planetary ball mill. Then it proceeded to the mechanical design and selection of each element that makes up the prototype, using simulation tools: SOLIDWORKS, ANSYS, ADAMS and SAP2000. Subsequently, the plans of the elements were developed through the elaboration of processes flowcharts, the construction and assembly of the prototype were carried out. The functional tests were performance tests with bronze, transmission steel and Steel ASTM A743, at a maximum supply capacity of 220 gr and a speed of 400 RPM for two, four and five hours, with 25 tempered steel balls of 20 mm during the first and second grinding hours, used in the remaining time 100 of φ10 mm. Afterward the powder was sieved having 153 gr of bronze between 0,6 to 0,06 mm and 69 gr ≤ to 0,06 mm of where the 57 , 14% is in a range of 2.49 to 9.74 μm, in the transmission there is 143 gr between 0.4 to 0.06 mm and 76 gr below these limits with 58.57% between 1, 02 to 4.72 μm, in the stainless 129 gr have from 1 to 0.06 mm where 86 g are smaller with 78.57% between 2.13 to 8.45 μm, it is concluded that if it is possible to obtain stainless steel metallic powder especially. It is suggested to follow the recommendations presented in order to expand this investigation.es_ES
dc.language.isospaes_ES
dc.publisherEscuela Superior Politécnica de Chimborazoes_ES
dc.relation.ispartofseriesUDCTFM;15T00704-
dc.rightsinfo:eu-repo/semantics/openAccesses_ES
dc.subjectTECNOLOGÍA Y CIENCIAS DE LA INGENIERÍAes_ES
dc.subjectVIRUTAes_ES
dc.subjectACERO ASTM A743es_ES
dc.subjectMOLIENDAes_ES
dc.subjectVELOCIDAD DE IMPACTOes_ES
dc.subjectPOLVO METÁLICOes_ES
dc.subjectTAMIZACIONes_ES
dc.subjectTAMAÑO DEL POLVOes_ES
dc.titleDiseño y construcción de un prototipo para la obtención de polvo metalico a partir de la viruta generada de los procesos de mecanizado del CIRT unidad de negocios Hidroagoyan.es_ES
dc.typebachelorThesises_ES
dc.contributor.miembrotribunalVillavicencio Cevallos, Julio César-
dc.rights.urihttps://creativecommons.org/licenses/by-nc-sa/3.0/ec/es_ES
Aparece en las colecciones: Ingeniero/a Mecánico/a

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
15T00704.pdf3,66 MBAdobe PDFVista previa
Visualizar/Abrir


Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons