dc.identifier.citationFlores Vaca, Gabriel Marcelo. (2021). Aprovechamiento de los residuos provenientes de la Industria Maderera “Buenaño” para la elaboración de hormigón.es_ES
dc.identifier.urihttp://dspace.espoch.edu.ec/handle/123456789/16831-
dc.descriptionEl presente trabajo de investigación tuvo como objetivo la utilización de residuos madereros de Eucalipto (Eucalyptus) de la Industria Maderera Buenaño ubicada en la cuidad de Riobamba, para la elaboración de hormigón mezclando éste con cemento y cal hidratada. La metodología constó de cuatro etapas, la primera fue la caracterización física del aserrín de Eucalipto mediante un análisis granulométrico obteniendo aserrín fino (partículas menores a 2mm) y aserrín grueso (partículas menores a 5mm y mayores a 2mm), pruebas de humedad presentando valores de 26,96 y 13,53 %, y, densidad con valores de 0,288 y 0,291 g/cm3 para aserrín fino y grueso respectivamente, la segunda etapa consistió en la elaboración de un diseño de mezclas con tres variables de entrada (composición de cemento, aserrín fino y aserrín grueso) y dos variables de respuesta (resistencia a la compresión y el peso) , elaborando nueve mezclas con contenido de cemento de 500, 550 y 600 kg/m3, y un contenido de aserrín en relación fino-grueso de 60/40, 50/50, y 40/60 para cada una. La tercera etapa consistió en la elaboración de muestras de dichas mezclas y realización de pruebas de resistencia a la compresión de las mismas. Finalmente se realizó un análisis estadístico con los resultados obtenidos en las pruebas experimentales con la ayuda del software Statgraphics, determinando que la mezcla que simultáneamente muestra una maximización en la resistencia a la compresión y una minimización del peso del hormigón es la mezcla C compuesta por una cantidad de cemento de 500 kg/m3 y una relación de aserrín fino- grueso de 40/60, presentando una resistencia a la compresión de 45,58 kg/cm2 y un peso de 2,31kg. Se recomienda realizar un estudio utilizando distintos tipos de cemento en el hormigón para determinar su influencia en los resultados finales.es_ES
dc.description.abstractThe aim of this research work was to use Eucalyptus (Eucalyptus) wood waste taken from Industria Maderera Buenaño located in Riobamba city for the production of concrete by mixing it with cement and hydrated lime. The methodology consisted of four steps, the first one was the physical characterization of the Eucalyptus sawdust by means of a granulometric analysis obtaining fine sawdust (particles smaller than 2mm) and coarse sawdust (particles smaller than 5mm and greater than 2mm), humidity tests showing values of 26.96 and 13.53%, and, density with values of 0.288 and 0.291 g/cm3 for fine and coarse sawdust respectively, the second step consisted of developing a design of mixtures with three input variables (cement composition, fine sawdust and coarse sawdust) and two response variables (compression strength and weight), making nine mixtures with a cement content of 500, 550 and 600 kg/m3 and sawdust content with a fine-to-coarse ratio of 60/40, 50/50, and 40/60 for each one. The third step consisted of preparing samples of previous mixtures and compression strength tests on them. Finally, a statistical analysis was carried out, results obtained in the experimental tests with the help of the Statgraphics software, determining that the mixture that simultaneously shows maximizing of compression strength and minimizing of concrete weight is the mixture C, composed of 500 kg/m3 cement with a ratio of fine-coarse sawdust of 40/60, presenting a compression strength of 45.58 kg/cm2 and a weight of 2.31 kg. It is recommended to carry out a study using different types of cement in the concrete to determine their influence on the final results.es_ES
dc.language.isospaes_ES
dc.publisherEscuela Superior Politécnica de Chimborazoes_ES
dc.relation.ispartofseriesUDCTFC;96T00733-
dc.rightsinfo:eu-repo/semantics/openAccesses_ES
dc.subjectTECNOLOGÍA Y CIENCIAS DE LA INGENIERÍAes_ES
dc.subjectINGENIERÍA QUÍMICAes_ES
dc.subjectHORMIGÓNes_ES
dc.subjectASERRÍNes_ES
dc.subjectCEMENTOes_ES
dc.subjectRESISTENCIA A LA COMPRESIÓNes_ES
dc.subjectMEZCLASes_ES
dc.subjectRESIDUOS MADEREROSes_ES
dc.titleAprovechamiento de los residuos provenientes de la industria maderera “Buenaño” para la elaboración de hormigónes_ES
dc.typeinfo:eu-repo/semantics/bachelorThesises_ES
dc.contributor.miembrotribunalGuamán Lozada, Darío Fernando-
dc.rights.urihttps://creativecommons.org/licenses/by-nc-sa/3.0/ec/es_ES
Aparece en las colecciones: Ingeniero/a Químico/a

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
96T00733.pdf1,35 MBAdobe PDFVista previa
Visualizar/Abrir


Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons