dc.identifier.citationPilataxi Pinduisaca, Ana Cristina. (2017). Utilización de precurtiente resínico en combinación con diferentes niveles de sulfato de aluminio para la curtición de pieles ovinas en la obtención de cuero para calzado. (Tesis de grado. Ingeniero en Industrias Pecuarias). Escuela Superior Politécnica de Chimborazo. Riobamba.es_ES
dc.identifier.urihttp://dspace.espoch.edu.ec/handle/123456789/7209-
dc.descriptionRESUMEN En el Taller de curtiembre de Pieles de la FCP, de la ESPOCH, se evaluó la curtición con diferentes niveles de sulfato de aluminio en combinación con precurtiente resínico en la obtención de cuero para calzado, utilizando 21 pieles ovinas que fueron distribuidas en 3 tratamientos y 7 repeticiones, modeladas con un diseño completamente al azar simple. Los resultados indican que el nivel adecuado de sulfato de aluminio que se combinara con el 3% de precurtiente resínico para curtir pieles ovinas consigue producir una materia prima para la confección de calzado libre de cromo, para evitar problemas de legislación ambiental a la empresa. Las mayor resistencia a la tensión (1217,95 N/cm2), y temperatura de encogimiento (64,86 °C), se consiguen al utilizar 7% de sulfato de aluminio (T1), mientras tanto que la mayor elongación fue alcanzada con 8% de curtiente sulfato de aluminio, permitiendo que el cuero cumpla con las normas técnicas. La mejor ponderación de llenura (4,71 puntos) y finura de flor (4,86 puntos), se consigue al curtir con mayores niveles de sulfato de aluminio (T3), mientras que la mejor blandura (4,57 puntos), es alcanzada con niveles más bajos de curtiente. La mayor rentabilidad se consigue al trabajar con 7% de sulfato de aluminio ya que la relación beneficio costo fue de 1,28; es decir que por cada dólar invertido se espera una ganancia de 28 centavos que es alta en relación al de otras actividades industriales similares que registran menores márgenes de utilidad y sobre todo involucran riesgos económicos mayores.es_ES
dc.description.abstractIn the Workshop, of: leather tannery of the FCP, of ESPOCH, was evaluated the tanning with different levels of aluminum sulphate in combination with resin resins in the production of leather for footwear, using 21 sheep skins that were distributed in 3 treatments and 7 replicates, modeled with a simple completely random design, The results indicate that the adequate level of aluminum sulphate combined with 3% pre-cured resinical to tanning ovine skins produces a raw material for the production of chromium-free footwear to avoid problems of environmental legislation to the company. The higher tensile strength (1217.95 N/cm2), and shrinkage temperature (64.86 ° C), are achieved by using 7% aluminum sulphate (T1), while the greater elongation was achieved with 8% tan aluminum sulphate, allowing leather to meet technical standards. The best weighting infilling (4.71 points) and flower fineness (4.86 points) is obtained when tanning with higher levels of aluminum sulphate (T3), while the best softness (4.57 points), is achieved with lower tanning levels. The highest profitability is achieved by working with 7% aluminum sulphate as the cost benefit ratio was 1.28; that is to say for each dollar invested a profit of 28 cents is expected that is high in relation to other similar industrial activities that register lower profit margins and above all involve greater economic risks.es_ES
dc.language.isospaes_ES
dc.publisherEscuela Superior Politécnica de Chimborazoes_ES
dc.relation.ispartofseriesUDCTFCP;27T0368-
dc.rightsinfo:eu-repo/semantics/openAccesses_ES
dc.subjectPRECURTIENTE RESÍNICOes_ES
dc.subjectSULFATO DE ALUMINIOes_ES
dc.subjectCURTICIÓN DE PIELES OVINASes_ES
dc.subjectPIELES OVINASes_ES
dc.subjectCUERO PARA CALZADOes_ES
dc.subjectRIOBAMBA (CANTÓN)es_ES
dc.subjectCHIMBORAZO (PROVINCIA)es_ES
dc.titleUtilización de precurtiente resínico en combinación con diferentes niveles de sulfato de aluminio para la curtición de pieles ovinas en la obtención de cuero para calzadoes_ES
dc.typebachelorThesises_ES
dc.contributor.miembrotribunalVillegas Freire, Cristina Nataly-
dc.rights.urihttps://creativecommons.org/licenses/by-nc-sa/3.0/ec/es_ES
Aparece en las colecciones: Ingeniero en Industrias Pecuarias; Ingeniero/a Agroindustrial

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
27T0368.pdf3,35 MBAdobe PDFVista previa
Visualizar/Abrir


Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons