Por favor, use este identificador para citar o enlazar este ítem:
http://dspace.espoch.edu.ec/handle/123456789/13812
Registro completo de metadatos
Campo DC | Valor | Lengua/Idioma |
---|---|---|
dc.contributor.advisor | Serrano Aguiar, Carlos Oswaldo | - |
dc.contributor.author | Aguirre Ruiz, Diana Estefanía | - |
dc.date.accessioned | 2020-02-18T16:08:34Z | - |
dc.date.available | 2020-02-18T16:08:34Z | - |
dc.date.issued | 2020-01-22 | - |
dc.identifier.citation | Aguirre Ruiz, Diana Estefanía. (2020). Análisis de la influencia del tamaño de las agujas de la martensita en las propiedades mecánicas de los aceros AISI 4140 y AISI 4340. Escuela Superior Politécnica de Chimborazo. Riobamba. | es_ES |
dc.identifier.uri | http://dspace.espoch.edu.ec/handle/123456789/13812 | - |
dc.description | Los avances tecnológicos y el desarrollo industrial han llevado a los ingenieros a buscar nuevas alternativas sobre el uso de los materiales, para esto uno de sus principales metas es controlar su comportamiento en la industria mediante la modificación de sus propiedades, con el siguiente trabajo de investigación se pretende analizar la influencia del tamaño de las agujas de martensita en las propiedades mecánicas de los Aceros AISI 4140 y AISI 4340, mediante un procedimiento que ayude a determinar la longitud y distribución de la martensita su microestructura, las muestras fueron templadas para obtener distintas agujas de martensita, luego de hacer el análisis metalográfico de las muestras, se calcula el tamaño de grano para determinar el diámetro promedio, que equivale a la longitud de las agujas de martensita principales, las mismas que crecen de borde a borde en los granos de austenita, posterior a esto se realizaron ensayos de dureza y tracción, obteniendo durezas de 45,8 HRC para una aguja de 0,026 mm siendo la más pequeña y 60,2 HRC para una longitud de 0,0378 mm que corresponde a la longitud más grande promedio de las muestras analizadas y alcanzando una resistencia a la tracción de 1451,3MPa y 1589,74MPa. Concluyendo que la dureza incrementa a medida que las agujas de martensita crecen, sucede lo contrario con los resultados de la resistencia a la tracción cuyo comportamiento es independiente de la microestructura martensítica, para ampliar la investigación sobre la influencia de las agujas de martensita en las propiedades mecánicas de los aceros, se recomienda obtener muestras con longitudes de agujas que varíen considerablemente, considerando que en esta investigación las granos de austenita van de 6.5 a 8.5. | es_ES |
dc.description.abstract | Technological advances and industrial development have led engineers to look for new alternatives on the use of materials, for this one of their main goals is to control their behaviour in the industry by modifying their properties. The following research work aims to analyse the influence of the size of martensite needles on the mechanical properties of AISI 4140 and AISI 4340, using a procedure that helps determine the length and distribution of martensite and its microstructure. To obtain different martensite needles it was necessary to temper the samples, after doing the metallographic analysis of the samples, it proceeds to calculate the grain size to determine the average diameter, which equals to the length of the main martensite needles, the same ones that grow from the edge on the edge of the austenite grains. After this, hardness and tensile tests were carried out, obtaining hardnesses of 45.8 HRC for a needle of 0.026 mm being the smallest and 60.2 HRC for a length of 0.0378 mm corresponding to the most considerable average length of the samples analysed and reaching a tensile strength of 1451.3MPa and 1589.74MPa. Concluding that the hardness increases as martensite needles grow, the opposite occurs with the results of tensile strength whose behaviour is independent of the martensitic microstructure, to extend the investigation into the influence of martensite needles on the properties mechanical steels, the recommendation is to obtain samples with needle lengths that vary considerably, considering that in this investigation the austenite grains range from 6.5 to 8.5. | es_ES |
dc.language.iso | spa | es_ES |
dc.publisher | Escuela Superior Politécnica de Chimborazo | es_ES |
dc.relation.ispartofseries | UDCTFM;15T00727 | - |
dc.rights | info:eu-repo/semantics/openAccess | es_ES |
dc.subject | TECNOLOGÍA Y CIENCIAS DE LA INGENIERÍA | es_ES |
dc.subject | INGENIERÍA MECÁNICA | es_ES |
dc.subject | ESTRUCTURA MARTENSÍTICA | es_ES |
dc.subject | MARTENSITA | es_ES |
dc.subject | PROPIEDADES MECÁNICAS | es_ES |
dc.subject | DUREZA | es_ES |
dc.subject | RESISTENCIA A LA TRACCIÓN | es_ES |
dc.title | Análisis de la influencia del tamaño de las agujas de la martensita en las propiedades mecánicas de los aceros AISI 4140 y AISI 4340. | es_ES |
dc.type | bachelorThesis | es_ES |
dc.contributor.miembrotribunal | Viteri Núñez, Edwin Fernando | - |
dc.rights.uri | https://creativecommons.org/licenses/by-nc-sa/3.0/ec/ | es_ES |
Aparece en las colecciones: | Ingeniero/a Mecánico/a |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
15T00727.pdf | 5,2 MB | Adobe PDF | ![]() Visualizar/Abrir |
Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons