dc.identifier.citationRodríguez Guambo, José Israel. (2021). Obtención y caracterización de espumas metálicas de aluminio funcionalmente graduadas mediante el método de infiltración en preformas solubles y su aplicación en elementos de deformación programada. Escuela Superior Politécnica de Chimborazo. Riobamba.es_ES
dc.identifier.urihttp://dspace.espoch.edu.ec/handle/123456789/14663-
dc.descriptionEste trabajo se efectuó bajo un protocolo experimental para la obtención de espumas metálicas de aluminio con una porosidad variada. El protocolo se basó en el método de infiltración en preformas solubles en agua; como material de preforma se empleó el óxido de sodio, con tamaños de 3, 5 y 7 mm respectivamente que fueron ubicados en forma de pirámide. Se realizó un análisis metalográfico para conocer las propiedades más relevantes de las espumas metálicas como son la densidad relativa, porosidad, espesor de ligamento. Resultado de este análisis se obtuvo en promedio una densidad relativa de las espumas de 0.49 y un porcentaje de porosidad en promedio del 51%, para conocer el espesor de ligamento se empleó el programa computacional Image J, y se obtuvo un espesor de 0.94, 1.5 y 1.8 mm aproximadamente para los diámetros de poro de 3, 5 y 7 mm respectivamente. Como parte de esta investigación, se realizó ensayo cuasiestático de compresión para obtener la energía absorbida mediante la integración del área bajo la curva esfuerzo-deformación. Para completar el ensayo mecánico, se llevó a cabo el ensayo dinámico de compresión mediante el impacto frontal de un péndulo diseñado para aplicaciones automotrices, con el objeto de medir la capacidad de absorción y porcentaje de deformación. Posteriormente se comparó dichos resultados con los del ensayo de compresión uniaxial. Finalmente, el resultado de la comparación muestra la gran capacidad de absorción de energía de deformación en este tipo de espumas y su funcionalidad en elementos de deformación programada.es_ES
dc.description.abstractThis work was carried out under an experimental protocol for obtaining aluminum metal foams with a varied porosity. The protocol was based on the method of infiltration into water soluble preforms; sodium oxide was used as preform material, with sizes of 3, 5 and 7 mm, respectively, which were placed in pyramid form. A metallographic analysis was performed to know the most relevant properties of metal foams such as relative density, porosity, ligament thickness. Result of this analysis was obtained on average a relative density of the foams of 0.49 and a percentage of porosity on average of 51%, to know the thickness of ligament was used the computer program Image J, and obtained a thickness of 0.94, 1.5 and 1.8 mm approximately for the pore diameters of 3, 5 and 7 mm respectively. As part of this research, quasi-static compression test was performed to obtain the absorbed energy by integrating the area under the stress-strain curve. To complete the mechanical test, the dynamic compression test was carried out by means of the frontal impact of a pendulum designed for automotive applications, in order to measure the absorption capacity and percentage of deformation. These results were then compared with those of the uniaxial compression trial. Finally, the result of the comparison shows the great absorption capacity of deformation energy in this type of foams and its functionality in programmed deformation elements.es_ES
dc.language.isospaes_ES
dc.publisherEscuela Superior Politécnica de Chimborazoes_ES
dc.relation.ispartofseriesUDCTIPEC;20T01415-
dc.rightsinfo:eu-repo/semantics/openAccesses_ES
dc.subjectDISEÑO MECÁNICOes_ES
dc.subjectMETALOGRÁFICOes_ES
dc.subjectESPUMAS METÁLICASes_ES
dc.subjectPOROSIDADes_ES
dc.subjectABSORBEDORES DE IMPACTOes_ES
dc.subjectENSAYO CUASIESTÁTICOes_ES
dc.titleObtención y caracterización de espumas metálicas de aluminio funcionalmente graduadas mediante el método de infiltración en preformas solubles y su aplicación en elementos de deformación programada.es_ES
dc.typeinfo:eu-repo/semantics/masterThesises_ES
dc.contributor.miembrotribunalLópez Ortiz, Santiago Alejandro-
dc.contributor.miembrotribunalSánchez Carrión, Edgar Fabián-
dc.rights.urihttps://creativecommons.org/licenses/by-nc-sa/3.0/ec/es_ES
Aparece en las colecciones: Maestrias: Modalidad Proyectos de Investigación y Desarrollo

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
20T01415.pdf2,72 MBAdobe PDFVista previa
Visualizar/Abrir


Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons